Chemical etching induced microporous nickel backbones decorated with metallic Fe@hydroxide nanocatalysts: an efficient and sustainable OER anode toward industrial alkaline water-splitting

초록

Development of cost-effective and highly efficient electrocatalysts for water splitting is crucial to produce affordable and sustainable green-hydrogen energy that can alleviate the current overreliance on fossil fuels. This work demonstrates the simple immersion-based chemical etching of nickel foam (NF) in an ethanolic FeCl3 solution to generate microporous nickel (Ni) backbones decorated with hierarchically structured metallic Fe doped Ni-Fe-hydroxide nanoparticles serving as a highly promising oxygen evolution reaction (OER) electrode in alkaline water. The optimally etched NF-based OER electrode exhibits a low Tafel slope of 47.3 mV dec(-1) and a low overpotential of 220, 270, and 310 mV at 10, 100, and 500 mA cm(-2), respectively. Intriguingly, this electrode also exhibits a perfectly reversible OER and HER performance between +400 and -40 mA cm(-2) with no evidence of electrode potential decay for 80 h. Importantly, when used with an industrial-type 30 wt% KOH aqueous electrolyte and compared to a benchmark Pt/C(20wt%)||IrO2-based cell, the electrolyzer exhibits a lower cell voltage of 1.52 (vs. 1.56 V of Pt/C(20wt%)||IrO2-cell), 1.62 (vs. 1.79), 1.69 (vs. 1.92) and 1.79 (vs. 2.08) V at 10, 50, 100, and 240 mA cm(-2), respectively, with the cell voltage maintained for similar to 100 h.

키워드