Sucrose-templated interconnected meso/macro-porous 2D symmetric graphitic carbon networks as supports for alpha-Fe2O3 towards improved supercapacitive behavior

초록

In this study, ultrahigh electrochemical performance for interconnected meso/macro-porous 2D C@alpha-Fe2O3 synthesized via sucrose-assisted microwave combustion is demonstrated. Hematite (alpha-Fe2O3) synthesized via the same approach gave an encouraging electrochemical performance close to its theoretical value, justifying its consideration as a potential supercapacitor electrode material; nonetheless, its specific capacitance was still low. The pore size distribution as well as the specific surface of bare alpha-Fe2O3 improved from 145 m(2) g(-1) to 297.3 m(2) g(-1) after it was coated with sucrose, which was endowed with ordered symmetric single-layer graphene (2D graphene). Accordingly, the optimized hematite material (2D C@alpha-Fe2O3) showed a specific capacitance of 1876.7 F g(-1) at a current density of 1 A g(-1) and capacity retention of 95.9% after 4000 cycles. Moreover, the material exhibited an ultrahigh energy density of 93.8 W h kg(-1) at a power density of 150 W kg(-1). The synergistic effect created by carbon-coating alpha-Fe2O3 resulted in modest electrochemical performance owing to extremely low charge transfer resistance at the electrode-electrolyte interface with many active sites for ionic reactions and efficient diffusion process. This 2D C@alpha-Fe2O3 electrode material has the capacity to develop into a cost-effective and stable electrode for future high-energy-capacity supercapacitors.

키워드