Hydrogen permeation properties of Pd-coated V89.8Cr10Y0.2 alloy membrane using WGS reaction gases

초록

The influence of co-existing gases on the hydrogen permeation was studied through a Pd-coated V89.8Cr10Y0.2 alloy membrane. Preliminary hydrogen permeation experiments have been confirmed that hydrogen flux was 6.26 ml/min/cm(2) for a Pd-coated V89.8Cr10Y0.2 alloy membrane (thick: 0.5 mm) using pure hydrogen as feed gas. Also, the hydrogen permeation flux decreased with decrease of hydrogen partial pressure at constant pressure when H-2/CO2 and H-2/CO2/H2S mixture applied as feed gas respectively and permeation fluxes were satisfied with Sievert's law in different feed conditions. It was found from XRD and SEM results after permeation test that the Pd-coated V89.8Cr10Y0.2 alloy membrane had good stability and durability for various mixture feeding conditions. Copyright (C) 2013, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.