Optical properties in Mn-doped ZnS thin films: Photoluminescence quenching

초록

Mn-doped ZnS thin films are synthesized on soda-lime glass substrates using magnetron co-sputtering technique. X-ray diffraction and atomic force microscopy measurements indicate that of the as-obtained films including the highest Mn (similar to 11% relative to the Zn concentration) in the lattice of ZnS are amorphous with a granular morphology. X-ray photoelectron spectroscopy reveals the presence of Zn2+, Mn2+ and S2- chemical states in the films. The undoped ZnS film exhibits photoluminescence (PL) peaks at energies around 3.26 eV (wavelength similar to 379 nm) and 2.95 eV (similar to 420 nm), which originate from the interplay between excited electron, defect (sulfur vacancy) states and the valence band. For the Mn-doped ZnS films, the band-to-band emission peak is quenched and shifts toward to higher energies at a rate of 11.7 +/- 2 meV/Mn%. We propose that Mn dopant-mediated structural phases and non-radiative deep traps in ZnS cause the modification in the optical transition. (C) 2015 Elsevier B.V. All rights reserved.

키워드