Facile preparation of three-dimensional hierarchical MgO microstructures for non-enzymatic glucose sensor

초록

Rational structural design plays a vital role in the continuous development of electrochemical activity in glucoseoxidizing materials, which is crucial for achieving high-performance glucose sensing. Herein, a threedimensional (3D) MgO microstructure was prepared using the hydrothermal treatment of precursors and inert gas calcination of hydrothermally produced nuclei. This 3D-MgO consisted of nanosheets with respective thicknesses and side lengths of - 50 nm and - 10 & mu;m that were strongly tied together. Structural analysis demonstrated the structure's high crystallinity and large surface area of 79.82 m2 & BULL;g- 1. Moreover, Mott-Schokky and valance band analyses revealed that 3D-MgO exhibited a suitable band-edge potential for redox activity, with conduction and valence band potentials of - 2.15 and 2.29 eV, respectively. Based on these excellent characteristics, the 3D MgO was utilized as a nonenzymatic glucose-oxidizing electrode, where it exhibited high sensitivity (198 & mu;A & BULL;mM- 1 & BULL;cm- 2), a quick response time (10 s), low detection limit (0.41 & mu;M), and a wide linear range (0.04-6.85 mM). Furthermore, it exhibited superb selectivity, repeatability, reproducibility with long-term high chemical stability, and a successful response to the glucose content present in human saliva. Due to these excellent material properties and outstanding performance in terms of glucose detection, 3D-MgO is a strong potential candidate for future research.

키워드