Effect of Zr substitution on photocatalytic and magnetic properties of lanthanum titanate

Abstract

The LaFe1-xZrxO3 (x = 0.01, 0.05) ceramics were prepared by sol-gel and annealing method and studied by XRD, Raman scattering analysis, SEM, and impedance spectroscopy method. The crystal structure and phonon characteristics analysis revealed that the crystal structure tends to preserve its ideal orthorhombic structure, following the increase in driving force of the Fe/ZrO6 octahedral tilting. The frequency-dependent dielectric parameters at each temperature decreased with increasing Zr content. The temperature dependence dielectric relaxation and dc conduction mechanism satisfied the Arrhenius law and increased with increasing Zr content. The activation energy ranged from 0.30 to 0.50 eV and was similar in the relaxation and conduction mechanisms, indicating that both transport mechanisms were based on a similar mechanism.